8114 Wrench, Striking Box Bent

The code No.8114 stainless steel striking box bent wrench is used to tighten or loosen bolts and nuts. The bent head makes it suitable for use where space is narrow or has deep concavity. It is made of stainless steel processed by drop forging.

304QF stainless steel tools technical parameters:
Chemical composition: %

Physical property
Tensile strength: σb(MPa)≥520
Offset yield strength:σ0.2(MPa)≥205
Elongation:δ5(%)≥40
Contraction percentage of area: z(%)=60
Density (20℃, g/cm3): 7.93
Hardness: HRC15-25
Melting point (℃): 1398~1454
Specific heat (0~100℃, KJ·kg-1K-1): 0.50
Heat conductivity (W·m-1·K-1): (100℃) 16.3, (500℃) 21.5
Linear expansion coefficient (10-6·K-1): (0~100℃) 17.2; (0~500℃) 18.4
Resistivity (20℃, 10-6Ω·m): 0.73
Magnetism: ≤5nT within 10cm in the magnetic field

2. Martensitic stainless steel (cutting tools stainless steel): representative grade: 420
The mechanical property of martensitic stainless steel is adjustable by heat treatment. Generally speaking, it is a type of hardenable stainless steel. It is hardened after quenching. Different tempering temperatures give different combinations of hardness and toughness. This stainless steel is widely used in such industries where the requirements of corrosion resistance is not very high, plus the cutting tools and machine elements have high requirements on strength.

420 stainless steel tools parameters:
Chemical composition: %

Physical property
Tensile strength: σb(MPa)≥365
Offset yield strength:σ0.2(MPa)≥440
Elongation:δ5(%)≥20
Contraction percentage of area: z(%)=50
Density (20℃, g/cm3): 7.75
Hardness: HRC35-45
Melting point (℃): 1427
Specific heat (25℃, J·kg-1K-1): 460
Heat conductivity (W·m-1·K-1): 24.9
Linear expansion coefficient (mm/℃): (at20-100℃)

Parameters: